Quote:
Originally Posted by Retlaw
I know what you mean about toughened glass, do you think a diamond saw would cut it.
Relaw.
|
Nope the process of toughening is to re-heat ordinary glass so that a thin film of it melts all over, this causes surface tension when it cools again, just the slightest chip causes the whole thing disintegrate into tiny cubes.